摘 要:Electro-spark deposition has been carried out on tire 35CrMo steel by filling and restoring the simulated slot specimens, and continuous surface coating with extra low porosity was obtained with proper parameters. The microstructure transformation and interface behavior of deposited joint were observed and analyzed. It shows that a transition region with 15μm in depth was obtained between base metal and deposited metal, and metallurgical bonding was achieved between restored base metal and deposition coating.