【簡(jiǎn)介】
摘要：綜述了中低溫化學(xué)鍍鎳的常用方法，包括超聲波法、脈沖化學(xué)鍍法、加速催化法、電子載體法、有機(jī)酸配位劑法和光化學(xué)法。介紹了近年來(lái)該工藝的研究進(jìn)展，總結(jié)了該領(lǐng)域的研究現(xiàn)狀并預(yù)測(cè)了發(fā)展方向。
關(guān)鍵詞：化學(xué)鍍鎳；中低溫；研究進(jìn)展
中圖分類號(hào)；TQl53．12 文獻(xiàn)標(biāo)志碼：A
文章編號(hào)：1004—227X(2009)05—0023—04 New development of the technology of middle and lowtemperature electroless nickel plating／／ZOU Jian-ping*LIU Xian-ze，XING Qiu-ju，WEI Da0—sheng，LIN Wan-feng，LIU Sheng·bin，LIANG Zhen，LI Guang—ming
Abstract：The commonly used methods of middle and lowtemperature electroless nickel plating were summarized，including plating assisted with ultrasonic and pulsed current，the addition of accelerators，electron carders and organic acid complexing agents，as well as photochemical methods．The recent research progress of the technology wasintroduced．The research status of the field was summed up and the development direction forecasted．
Keywords：electroless nickel plating；middle and lowtemperature；research progress
First-author’S address：School of Environment and Chemical Engineering， Nanchang Hangkong University，Nanchang 330063，China
1 前言
化學(xué)鍍鎳技術(shù)具有鍍層均勻，耐磨性、耐腐蝕性好，硬度高，操作方便等優(yōu)點(diǎn)，適用于各種材料(包括非金屬材料)、復(fù)雜零件的施鍍，廣泛應(yīng)用于石油、化工、汽車、電子、食品等領(lǐng)域。以硫酸鎳作為主鹽、次磷酸鹽作為還原劑的化學(xué)鍍液，通常分為酸性和堿性鍍液2種。堿性鍍液具有鍍速快、施鍍溫度低、能耗少、鍍層光亮度好等特點(diǎn)，但其穩(wěn)定性較差，得到的化學(xué)鍍鎳層微結(jié)構(gòu)通常是片狀的，微晶尺寸較大，晶粒間會(huì)產(chǎn)生孔隙甚至晶界；而酸性化學(xué)鍍鎳層是層狀或顆粒狀結(jié)構(gòu)，可達(dá)到無(wú)孔隙，因而其耐磨性、耐蝕性以及硬度都比堿性化學(xué)鍍鎳層優(yōu)越。因此，越來(lái)越多的研究者致力于酸性化學(xué)鍍鎳工藝的研究。目前，工業(yè)生產(chǎn)中普遍使用的鍍液的操作溫度為85～
降低化學(xué)鍍鎳的施鍍溫度，不僅可以降低施鍍成本，提高鍍液穩(wěn)定性，而且便于加熱時(shí)控制溫度，方便現(xiàn)場(chǎng)施工操作[6-7]。因此，中低溫化學(xué)鍍鎳工藝成為當(dāng)前化學(xué)鍍領(lǐng)域的研究熱點(diǎn)課題。
|
|
|
|
|
|
|
|
|
|